Constantan Waea Papatahi Parani Konukura Alloy 6j40 Ribbon 0.4*2mm Whakaahua Whakaatu

Constantan Flat Waea Copper Nickel Alloy 6j40 Ribbon 0.4*2mm

Whakaahuatanga Poto:

Constantan Flat Waea Copper Nickel Alloy 6j11 Ribbon 0.4*2mm

Te ātete (200C μ Ω. m):0.1
Max. Te Mahana Mahi (0C):200
Te Kaha Toka (Mpa):≥ 250
Ira whakarewa (0C):1095
Kiato (g/cm3):8.9
TCR x10-6/ 0C (20~600 0C): <100

Tiwhikete:ISO 9001

Rahi:Whakaritea

ingoa hua:Koraha Konukura 6j11

tono:ahumahi

rauemi:koranu

āhuatanga:ātete teitei

mahi:pai te pumau o te ahua

taumaha:i runga

inenga:hei whakaritenga a te kiritaki

tae:parauri

āhua:waea

MOQ:20kg

Tukuna he imeera ki a matou

Taipitopito Hua

FAQ

Tohu Hua

New Constantan Flat Waea Copper Nickel Alloy 6j11 Ribbon 0.4*2mm

Te ahuatanga	Te ātete (200C μ Ω. m)	Max. Te Mahana Mahi (0C)	Te Kaha Tana (Mpa)	Ira whakarewa (0C)	Kiato (g/cm3)	TCR x10-6/ 0C (20~600 0C)	EMF vs Cu (μ V/ 0C) (0~100 0C)
Whakaingoa Alloy
NC003 (CuNi1)	0.1	200	≥ 250	1095	8.9	< 100	-12

Āhuatanga ā-tinana	Inenga	Nga korero
Kiato	8.94 g/cc
Nga Taonga Miihini	Inenga	Nga korero
Te Kaha Tensile, Mutunga	262 – 531 MPa
Te Kaha Tensile, Tukua	276 – 524 MPa	I runga i te riri
Elongation at Break	46.0 %	i roto i te 50.8 mm.
Modulus of Elasticity	115 GPa
Poissons Ratio	0.310	Kua tātaihia
Te mahi miihini	20 %	UNS C36000 (parahe tapahi kore utu) = 100%
Kōwae kutikuti	44.0GPa
Nga Taonga Hiko	Inenga	Nga korero
Te Atete Hiko	0.0000120 ohm-cm @Pamahana 20.0 ° C
Ngaa Waiariki	Inenga	Nga korero
CTE, raina	17.5 µ m/m-° C @Pamahana 20.0 – 300 ° C
Te Kaha Wera Motuhake	0.380 J/g-° C
Te Whakawhitinga Ngawha	64.0 W/mK @Pamahana 20.0 ° C
Te Whakarewarewa	< = 1125 ° C	Liquidus
Liquidus	1125 ° C
Tukatuka Rawa	Inenga	Nga korero
Te Mahana Whakawhana	565 – 815 ° C
Te Pawera Mahi-Whana	815 – 950 ° C
Nga Huānga Waahanga	Inenga	Nga korero
Parahi, Cu	> = 91.2 %
Rino, Fe	1.30 – 1.70 %
Arataki, Pb	< = 0.050 %
Manganese, Mn	0.30 – 0.80 %
Nickel, Ni	4.80 – 6.20 %
Zinc, Zn	< = 1.0 %

CuNi44 Ihirangi matū, %

Ni	Mn	Fe	Si	Cu	Ētahi atu	Tohutohu ROHS
						Cd	Pb	Hg	Cr
44	1%	0.5	-	Bal	-	ND	ND	ND	ND

Nga Taonga Miihini

Max Tonu Ratonga Temp	400ºC
Te parenga i te 20ºC	0.49±5%ohm mm2/m
Kiato	8.9 g/cm3
Te Whakawhitinga Ngawha	-6(Mōrahi)
Te Whakarewarewa	1280ºC
Te Kaha Toka,N/mm2 Kua Ahia, Ngawari	340~535 Mpa
Te Kaha Toka,N/mm3 Huri Matao	680~1070 Mpa
Whakaroa(anneal)	25%(Min)
Te whakaroa	≥Min)2%(Min)
EMF vs Cu, μV/ºC (0~100ºC)	-43
Hangahanga Micrographic	austenite
Taonga aukume	Kore